Abstract
This work reports the use of cross-linkers in bio-based blends from hydroxypropyl-modified lignin (TcC) and a bio-based polyamide (PA1010) for possible use as carbon fibre precursors, which, while minimising their effects on melt processing into filaments, assist in cross-linking components during the subsequent thermal stabilisation stage. Cross-linkers included a highly sterically hindered aliphatic hydrocarbon (Perkadox 30, PdX), a mono-functional organic peroxide (Triganox 311, TnX), and two different hydroxyalkylamides (Primid® XL-552 (PmD 552) and Primid® QM-1260 (PmD 1260)). The characterisation of melt-compounded samples of TcC/PA1010 containing PdX and TnX indicated considerable cross-linking via FTIR, DSC, DMA and rheology measurements. While both Primids showed some evidence of cross-linking, it was less than with PdX and TnX. This was corroborated via melt spinning of the melt-compounded chips or pellet-coated TcC/PA1010, each with cross-linker via a continuous, sub-pilot scale, melt-spinning process, where both Primids showed better processability. With the latter technique, while filaments could be produced, they were very brittle. To overcome this, melt-spun TcC/PA1010 filaments were immersed in aqueous solutions of PmD 552 and PmD 1260 at 80 °C. The resultant filaments could be easily thermally stabilised and showed evidence of cross-linking, producing higher char residues than the control filaments in the TGA experiments.